Biocompatibility of bismuth silicate coatings deposited on 316L stainless steel by sol-gel process

Abstract

Bismuth silicate, (BSO) thin films have been fabricated by sol–gel process. The stable sol was synthesized by using bismuth nitrate (III) pentahydrate and tetraethyl orthosilicate (TEOS). The films were deposited by spin-coating at 1500 rpm on Stainless Steel 316L. The films were characterized by Atomic Force Microscopy (AFM), Scanning Electron Microscopy (SEM), X-ray diffraction (XRD) besides the measured of the films thickness. This study aimed to evaluate the cell adhesion and cellular proliferation of osteoblast cells on BSO thin films and substrate 316L by MTT assay. It is concluded that the growth of osteoblasts is homogeneous in the surface of the coatings indicating that the medium offered by the films does not present active cytotoxicity and exceed in large number the level of cellular growth compared to Stainless Steel

Películas delgadas de silicato de bismuto (BSO) se han fabricado mediante el proceso sol-gel. El sol estable se sintetizó utilizando nitrato de bismuto (III) pentahidrato y tetraetil-ortosilicato (TEOS). Las películas fueron depositadas a 1500 rpm mediante la técnica de centrifugado. Los recubrimientos se caracterizaron por microscopía de fuerza atómica (AFM), microscopía electrónica de barrido (SEM), difracción de rayos-X (DRX) y se midió el espesor de las películas. El objetivo de este estudio fue evaluar la adhesión y la proliferación en células de osteoblastos, mediante el ensayo MMT, al incubarse sobre películas BSO en sustratos de 316L. Se concluyó que el crecimiento de los osteoblastos es homogéneo en la superficie de las películas, indicando que el medio ofrecido por los recubrimientos no presenta actividad citotóxica y favorece los niveles de crecimiento celular en comparación con los resultados obtenidos para los sustratos de acero inoxidable