Se presentan los resultados de la caracterización físico-cerámica, microquímica y estructural de muestras cerámicas de arcilla roja inmersas en soluciones de SiO2 – TiO2 – ZrO2 obtenidas por el método Sol-Gel utilizando ...

The metropolitan area of Cúcuta (Colombia) is characterized by the existence of several companies dedicated to the manufacture of ceramic construction materials. The existence of these companies is caused by the ...

Caracterización de cerámicos inmersos en soluciones del sistema sio2 – tio2 – zro2 sintetizadas por el método sol-gel
...
Sanchez Molina, Jorge | 2017-05-30

Se presentan los resultados de la caracterización físico-cerámica, microquímica y estructural de muestras cerámicas de arcilla roja inmersas en soluciones de SiO2 – TiO2 – ZrO2 obtenidas por el método Sol-Gel utilizando tetraetil ortosilacato, tetrabutóxido de titanio y tetrabutóxido de zirconio. Las muestras cerámicas fueron elaboradas con polvos atomizados de arcilla roja, cocidas a 1000°C. Después de la cocción las cerámicas fueron inmersas en las soluciones en concentraciones en volumen 10/20/70: Si/Ti/Zr y 10/70/20: Si/Ti/Zr con tiempos de permanencia de 2, 4 y 6 minutos. Posterior al secado las muestras se trataron térmicamente a 600°C durante 60 minutos, a una velocidad de 2°C/min. Aspectos microquímicos y microestructurales de las muestras cocidas fueron establecidos mediante el uso de difracción de rayos X (DRX), espectroscopia de infrarrojo (FTIR) y detección de energías dispersivas de rayos X (EDX). Las propiedades tecnológicas evaluadas fueron la absorción de agua, densidad aparente y resistencia mecánica a la flexión. El estudio permitió establecer que las muestras inmersas en la solución 10/70/20: Si/Ti/Zr permiten incrementar la resistencia mecánica a la flexión. De igual manera se observó una ligera reducción del porcentaje de absorción de agua con este mismo tratamiento. El tratamiento con mayor presencia de zirconio no muestra cambios significativos respecto al patrón empleado (muestra sin inmersión)

LEER
Metodología de conformación de lotes de arcilla para la industria cerámica del área metropolitana de Cúcuta a partir de análisis fisicoquímicos y modelado de mezclas
...
Blanco Meneses, Duvin Smith | 2020-01-01

The metropolitan area of Cúcuta (Colombia) is characterized by the existence of several companies dedicated to the manufacture of ceramic construction materials. The existence of these companies is caused by the high availability of red clays of sedimentary type that abound in this territory. Due to the goodness of the clay in the region, many entrepreneurs do not carry out activities aimed at obtaining a homogeneous raw material to be used in the manufacturing process of tiles, roof tiles and masonry ceramics. Although this fact does not have major disadvantages for the production that is sold in the local and national market, the same does not happen for the sales abroad, due to the variability between production batches caused by lack of homogeneity of the raw material used. From this problematic the authors developed this study with the purpose of finding a methodology that allows to reduce the heterogeneity of the argillaceous raw materials. The work consisted in making a comparative analysis between the methodology of random cutting with cone type homogenization and the mechanized trench methodology. Chemical analysis was carried out by X-ray fluorescence, mineralogical characterization by means of X-ray diffraction and physical-ceramic characterization (sand percentage, firing shrinkage and mechanical resistance to flexion) based on the guidelines of the Colombian technical standard for this kind of materials. It was evidenced that the trench methodology allows greater homogeneity in the results of the technological variables evaluated.

LEER

Repositorio Digital

Browsing by Subject "Arcilla roja"

Caracterización de cerámicos inmersos en soluciones del sistema sio2 – tio2 – zro2 sintetizadas por el método sol-gel

Metodología de conformación de lotes de arcilla para la industria cerámica del área metropolitana de Cúcuta a partir de análisis fisicoquímicos y modelado de mezclas

Envíos recientes

Caracterización de cerámicos inmersos en soluciones del sistema sio2 – tio2 – zro2 sintetizadas por el método sol-gel

Metodología de conformación de lotes de arcilla para la industria cerámica del área metropolitana de Cúcuta a partir de análisis fisicoquímicos y modelado de mezclas

Portales Institucionales

Enlaces de Interés

Contactos

Browsing by Subject "Arcilla roja"

Caracterización de cerámicos inmersos en soluciones del sistema sio2 – tio2 – zro2 sintetizadas por el método sol-gel ﻿

Metodología de conformación de lotes de arcilla para la industria cerámica del área metropolitana de Cúcuta a partir de análisis fisicoquímicos y modelado de mezclas ﻿

Envíos recientes

Caracterización de cerámicos inmersos en soluciones del sistema sio2 – tio2 – zro2 sintetizadas por el método sol-gel

Metodología de conformación de lotes de arcilla para la industria cerámica del área metropolitana de Cúcuta a partir de análisis fisicoquímicos y modelado de mezclas

Portales Institucionales

Caracterización de cerámicos inmersos en soluciones del sistema sio2 – tio2 – zro2 sintetizadas por el método sol-gel

Metodología de conformación de lotes de arcilla para la industria cerámica del área metropolitana de Cúcuta a partir de análisis fisicoquímicos y modelado de mezclas