En este trabajo se presenta la síntesis y la evaluación de la resistencia a la corrosión de recubrimientos de SiO2-TiO2-ZrO2-BiO2 depositados por la técnica de centrifugado sobre acero inoxidable AISI 316L. Los soles se ...

This report shows the synthesis and corrosion resistance of SiO2-TiO2-ZrO2-Bi2O3 coatings deposited by means of spin-coating on Ti6Al4V alloy. The sols were prepared from a mixture of organic precursors, tetraethoxysilane ...

Synthesis and corrosion resistance evaluation of coatings of SiO2-TiO2-ZrO2-BiO2 on 316L stainless produced by sol-gel
...
Olaya, Jhon | 2018-10

En este trabajo se presenta la síntesis y la evaluación de la resistencia a la corrosión de recubrimientos de SiO2-TiO2-ZrO2-BiO2 depositados por la técnica de centrifugado sobre acero inoxidable AISI 316L. Los soles se prepararon a partir de una mezcla de precursores orgánicos, como el tetraetoxisilano (TEOS) al 98%, tetrabutóxido de titanio (TBT) al 97%, zirconio (IV) butóxido (TBZ) al 80% en solución 1-butanol y nitrato de bismuto penta-hidratado Bi(NO3)3*5H2O. La resistencia a la corrosión se determinó mediante ensayos de curvas de polarización potenciodinámica y de espectroscopia de impedancia electroquímica (EIS) en una solución electrolítica de 3,5% Wt de NaCl + 0,5 M de H2SO4. A los soles preparados se les caracterizó mediante estudio reológico, de pH en función del tiempo, mediciones de espectroscopia de infrarrojo por transformada de Fourier (FTIR) y calorimetría diferencial de barrido (DSC). Los recubrimientos se caracterizaron mediante difracción de rayos X (XRD), microscopia electrónica de barrido (MEB), espectroscopia de energías dispersivas (EDX), fluorescencia de rayos X (XRF) y medidas de adherencia. Los resultados mostraron que las películas ofrecen una buena resistencia a la corrosión sobre el sustrato metálico disminuyendo los valores de densidades de corriente hasta en un orden de magnitud

LEER
Synthesis and corrosion resistance of SiO2-TiO2-ZrO2-Bi2O3 coatings spin-coated on Ti6Al4V alloy
...
Alférez Vega, Fabio Leonardo | 2018-02

This report shows the synthesis and corrosion resistance of SiO2-TiO2-ZrO2-Bi2O3 coatings deposited by means of spin-coating on Ti6Al4V alloy. The sols were prepared from a mixture of organic precursors, tetraethoxysilane (TEOS) 98%, titanium tetrabutoxide (TBT) 97%, Zirconium (IV) butoxide (TBZ) 80% in 1-butanol solution, and bismuth nitrate pentahydrate Bi (NO3)3 * 5H2O. The coatings were evaluated via potentiodynamic polarization and electrochemical impedance spectroscopy (EIS) tests in an electrolytic solution of 3.5% wt NaCl + 0.5 M H2SO4. The rheology and pH of the prepared sols were studied through rheology, pH as a function of time, Fourier transform infrared spectroscopy (FTIR), and differential scanning calorimetry (DSC) analysis. The coatings were characterized via X-ray diffraction (XRD), scanning electron microscopy equipped with dispersive energy spectroscopy (SEMEDX), X-ray fluorescence (XRF), and adhesion measurements. The results showed that the films add good corrosion resistance to the metal substrate, decreasing current densities up to one order of magnitude.

LEER

Repositorio Digital

Listar por tema "Adherence"

Synthesis and corrosion resistance evaluation of coatings of SiO2-TiO2-ZrO2-BiO2 on 316L stainless produced by sol-gel

Synthesis and corrosion resistance of SiO2-TiO2-ZrO2-Bi2O3 coatings spin-coated on Ti6Al4V alloy

Envíos recientes

Synthesis and corrosion resistance evaluation of coatings of SiO2-TiO2-ZrO2-BiO2 on 316L stainless produced by sol-gel

Synthesis and corrosion resistance of SiO2-TiO2-ZrO2-Bi2O3 coatings spin-coated on Ti6Al4V alloy

Portales Institucionales

Enlaces de Interés

Contactos

Listar por tema "Adherence"

Synthesis and corrosion resistance evaluation of coatings of SiO2-TiO2-ZrO2-BiO2 on 316L stainless produced by sol-gel ﻿

Synthesis and corrosion resistance of SiO2-TiO2-ZrO2-Bi2O3 coatings spin-coated on Ti6Al4V alloy ﻿

Envíos recientes

Synthesis and corrosion resistance evaluation of coatings of SiO2-TiO2-ZrO2-BiO2 on 316L stainless produced by sol-gel

Synthesis and corrosion resistance of SiO2-TiO2-ZrO2-Bi2O3 coatings spin-coated on Ti6Al4V alloy

Portales Institucionales

Synthesis and corrosion resistance evaluation of coatings of SiO2-TiO2-ZrO2-BiO2 on 316L stainless produced by sol-gel

Synthesis and corrosion resistance of SiO2-TiO2-ZrO2-Bi2O3 coatings spin-coated on Ti6Al4V alloy