@ARTICLE{Gar_In _2017,
author = "García-Páez, Ismael H. - de Aza, Antonio H. - Parra, Juan - Baudin, Carmen - Martín, M. Rocío - Pena, Pilar",
title = "In vitro study of the proliferation and growth of human fetal osteoblasts on Mg and Si co-substituted tricalcium phosphate ceramics",
abstract = "The objective of this work was to study the feasibility of the solid state sintering, a conventional ceramic processing method, to obtain Mg and Si co-substituted tricalcium phosphate bioceramics and composites containing diopside. A series of new Ca3(PO4)2 based ceramics has been prepared from attrition milled mixtures of synthetic Ca3(PO4)2 and CaMg(SiO3)2 powders, isostatically pressed and sintered at 1250–1300°C. Materials containing 0, 1, and 5 wt % of CaMg(SiO3)2 were constituted by β + α - Ca3(PO4)2 solid solutions while the material containing 60 wt % of CaMg(SiO3)2 was a constituted by β- Ca3(PO4)2 and CaMg(SiO3)2. The biological responses of the developed ceramics were studied in vitro using human fetal osteoblast cultures. Culture times ranged from 1 to 21 days. The new family of materials promotes the adhesion and proliferation of human osteoblasts cultured onto their surface forming a monolayer and showing a normal morphology. The results of the MTT and Alamar Blue assays showed that the soluble components extracted from the Mg/Si- co-substituted Ca3(PO4)2 and the Ca3(PO4)2-CaMg(SiO3)2 composite were noncytotoxic. The specimens with diopside exhibited a better in vitro behavior which is attributed to the release of Si and Mg ions to the culture medium, enhancing the activity of cells. © 2017 Wiley Periodicals, Inc. J Biomed Mater Res Part A: 105A: 2266–2275, 2017.",
year = 2017,
publisher = "Journal of Biomedical Materials Research Part A",
url = "https://repositorio.ufps.edu.co/handle/ufps/640",
}